Heavy oil thermal mainly depends on the injected high temperature steam to improve the heavy oil temperature, reduce the viscosity of heavy oil, and make heavy oil flow easily, so as to facilitate the heavy oil out. 
There are two main ways: 1) steam stimulation method, 2) steam flooding method.
In the high temperature working environment, the first consideration should be given to the material yield strength, tensile strength, plastic deformation; at the same time, need to consider the metal in a long time constant temperature, constant loading slowly to generate plastic deformation phenomenon-creep. This deformation may cause metal material creep fracture crack.
Product characteristics:
Under the condition of high temperature and short time, the tensile property is high. When the temperature rises up, the drop of property is small.
Application scope:
Suitable for wells working condition of 350℃, for a long time continuous use of thermal wells oilfield conditions.
Performance control
Tensile properties :

Grade	Room temperature			350℃
	Mpa Yield strength	Mpa Tensile strength	Elongation %	Mpa Yield strength
JST80H	552~758	≥689	Refer to API 5CT	≥500
JST100H	690~897	≥793		≥650
JST110H	758~965	≥862		≥700

Impact properties:(Note:refer to API SPEC 5CT)

Grade	Room temperature
	Longitudinal average value	Transverse average value
JST80H	27	14
JST100H	34	17
JST110H	41	20

 
Creep properties:(Note: stress 300Mpa)

Grade	Temperature	%/h The steady creep rate
JST80H	350℃	≤5*10-5
JST100H
JST110H